Material:
Outer: Irradiation crosslinked modified polyolefin material
Shrink ratio: 6: 1
Features:
- 6:1 high rate of heat shrinkage characteristics, the diameter was larger quilt coverage;
- Black sleeving, has excellent UV resistance;
- semi-rigid walled polyolefin material has excellent electrical insulation properties and mechanical protection properties;
- Minimum fully shrink temperature: 135 ℃.
Application: High magnification of the polyolefin heat shrinkable tubing material with good electrical insulation properties and mechanical protection properties, the 6:1 high rate of shrinkage characteristics, especially suitable for an extremely wide range of sizes harness connection or component connection.
Introduction
Item | Test method | Indicator |
Range of continuous operating temperature | IEC216 | -50℃~110℃ |
Tensile strength | ASTM D2671 | ≥13MPa |
Elongation at break | ASTM D2671 | ≥400% |
Tensile strength after aging | ASTM D2671(150℃) | ≥12MPa |
Elongation at break after aging | ASTM D2671(150℃) | ≥300% |
Volume resistivity | IEC93 | ≥1.0×10¹⁴ Ω· cm |
Breakdown strength | IEC243 | ≥20kV/mm |
Breakdown strength | ASTM D2671 | by |
Axial shrinkage | UL224 | 0~10% |
Concentricity rate | ASTM D2671 | ≥65% |
Cracking resistance | ASTM D1693(50℃) | No cracking |
Water absorption | ISO62(23℃,14day) | ≤0.2% |
Hot melt adhesive (single-wall type sixfold thick-walled tube does not involve) | ||
Softening Point | ASTM DE28 | 85℃ |
Peel strength(PE)) | DIN30672 | ≥4N/cm |
Copper stability | ASTM D2671 | No corrosion |
Antibacterial | ISO846 | by |
Specification
Specification | Product inner diameter(mm) | After shrinking the inner diameter(mm) | Wall thickness after shrinking(mm) | Standard length(mm) |
19.0/3.2 | 19.0 | 3.2 | 3.2 | 1000-1220 |
33.0/5.5 | 33.0 | 5.5 | 3.4 | 1000-1220 |
44.4/7.7 | 44.4 | 7.4 | 3.6 | 1000-1220 |
50.8/8.3 | 50.8 | 8.3 | 4.3 | 1000-1220 |
69.8/11.7 | 69.8 | 11.7 | 4.8 | 1000-1220 |
88.9/17.1 | 88.9 | 17.1 | 4.8 | 1000-1220 |
119.4/22.9 | 119.4 | 22.9 | 4.8 | 1000-1220 |